钢纤维混凝土断裂过程激光实时全息干涉法研究

刘冬梅1,2,宋超业3,陈志勇4   

  1. 1.北京科技大学 土木与环境工程学院,北京 100083; 2.浙江理工大学 建筑工程学院, 杭州 310018; 3.中铁隧道勘测设计院有限公司, 洛阳 471009; 4.广东省重工建筑设计院,广州 510030
  • 收稿日期:2005-12-26 出版日期:2007-09-10 发布日期:2013-10-15
  • 作者简介:刘冬梅,女,1964年生,博士研究生,教授,主要从事土木工程方面的教学与研究

Research on deformation and failure of steel fiber concrete by real-time laser holographic interferometry

LIU Dong-mei1,2, SONG Chao-ye3, CHEN Zhi-yong4   

  1. 1.School of Civil and Environmental Engineering, University of Science and Technology Beijing, Beijing 100083, China; 2.School of Civil Engineering and Architecture, Zhejiang Sci-Tech University, Hangzhou 310018, China; 3. China Railway Tunnel Survey & Design Institute Co. Ltd., Luoyang 471009, China; 4. Guangdong Design Institute of Heavy Industry & Architecture, Guangzhou 510030, China
  • Received:2005-12-26 Online:2007-09-10 Published:2013-10-15

摘要: 应用激光实时全息干涉法实现了钢纤维混凝土三点弯曲切口梁断裂全过程的实时动态观测研究,连续动态捕获了钢纤维混凝土试件的干涉条纹图。实时全息干涉条纹的动态特征和分布规律直观准确地演示了钢纤维混凝土的初裂点和各阶段的变形特征以及裂缝扩展全过程。试验研究表明,当混凝土试件的钢纤维掺量大于1.0 %时,钢纤维的阻裂增韧效应是明显的。钢纤维混凝土断裂力学参量的计算与分析显示,断裂能是反映钢纤维阻裂效应的敏感参数,用全息干涉条纹图的判识和用断裂能描述获得的试件断裂行为是一致的,激光实时全息干涉法能够为混凝土断裂力学研究提供可靠的试验支撑。

关键词: 实时全息干涉法, 动态干涉条纹, 钢纤维混凝土, 断裂过程, 断裂能

Abstract: Laser real-time holographic interferometry is applied to research the whole failure process of three-point bending beams of steel fiber concrete(SFC). The real-time holograms of crack growth on SFC beams are continuously captured. According to the active fringe’s movement and distribution on the SFC specimens as well as the hologram’s interpretation, the initiation and development of crack in SFC and its deforming character can be exactly visually shown. The experiment indicates the effect of steel fiber preventing fracture and increasing toughness is obvious while the content of steel fiber in concrete specimens is higher than 1.0 %. Based on the calculation of fracture parameters and its analysis, It is clearly revealed that fracture energy is a sensitive parameters for reflecting the effect of steel fiber preventing fracture.The fracture behaviour of the SFC specimens demonstrated by active fringes distribution is in accordance with the result from the explanation of fracture energy in SFC. Laser real-time holographic interferometry can provide an effective experimental support for concrete fracture mechanics.

Key words: real-time holographic interferometry, active fringe;steel fiber concrete, failure process, fracture energy

中图分类号: 

  • TU 377.9
[1] 徐栋栋, 邬爱清, 李 聪, 汪 斌, 蒋昱州, 曾 平, 杨永涛, . 破裂全过程模拟的改进非连续变形分析方法[J]. 岩土力学, 2019, 40(3): 1169-1178.
[2] 姚哨峰,张振南,葛修润,邱一平,徐金明,. 大理岩断裂能与细观结构几何特征相关性[J]. , 2016, 37(8): 2341-2346.
[3] 袁会娜,张 骏,张其光. 掺砾黏土拉伸断裂细观特性研究[J]. , 2016, 37(11): 3096-3104.
[4] 薛云亮,李庶林,林 峰,徐宏斌. 考虑损伤阀值影响的钢纤维混凝土损伤本构模型研究[J]. , 2009, 30(7): 1987-1992.
[5] 徐礼华,池 寅,李荣渝,苏 洁. 钢纤维混凝土深梁非线性有限元分析在ANSYS中的实现[J]. , 2008, 29(9): 2577-2582.
[6] 王春来,徐必根,李庶林,唐海燕. 单轴受压状态下钢纤维混凝土损伤本构模型研究[J]. , 2006, 27(1): 151-154.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
[1] 祝云华,刘新荣,舒志乐. 对“‘深埋隧道开挖围岩失稳突变模型研究’讨论”的答复[J]. , 2009, 30(10): 3215 -3216 .
[2] 刘小文,常立君,胡小荣. 非饱和红土基质吸力与含水率及密度关系试验研究[J]. , 2009, 30(11): 3302 -3306 .
[3] 王观石,李长洪,陈保君,李世海. 应力波在非线性结构面介质中的传播规律[J]. , 2009, 30(12): 3747 -3752 .
[4] 刘远明,夏才初. 直剪条件下非贯通节理岩体岩桥力学性质弱化机制及贯通模型初步研究[J]. , 2010, 31(3): 695 -701 .
[5] 高 阳,张庆松,徐帮树,李 伟. 海底采煤顶板支承压力分布规律与影响因素研究[J]. , 2010, 31(4): 1309 -1313 .
[6] 万少石,年廷凯,蒋景彩,栾茂田. 边坡稳定强度折减有限元分析中的若干问题讨论[J]. , 2010, 31(7): 2283 -2288 .
[7] 闫 铁,李 玮,毕雪亮. 基于分形方法的多孔介质有效应力模型研究[J]. , 2010, 31(8): 2625 -2629 .
[8] 刘 嘉,王 栋. 正常固结黏土中平板锚基础的吸力和抗拉力[J]. , 2009, 30(3): 735 -740 .
[9] 徐维生,柴军瑞,陈兴周,孙旭曙. 岩体裂隙网络非线性非立方渗流研究与应用[J]. , 2009, 30(S1): 53 -57 .
[10] 赵尚毅,郑颖人,李安洪,邱文平,唐晓松,徐 俊. 多排埋入式抗滑桩在武隆县政府滑坡中的应用[J]. , 2009, 30(S1): 160 -164 .