淋滤条件下GGBS-MgO固化铅污染黏土强度与溶出特性研究

薄煜琳1, 2，于博伟1, 2，杜延军1, 2，魏明俐1, 2   

  1. 1.东南大学 岩土工程研究所，江苏 南京 210096；2.东南大学 江苏省城市地下工程与环境安全重点实验室，江苏 南京 210096
  • 收稿日期:2014-12-31 出版日期:2015-10-10 发布日期:2018-06-13
  • 作者简介:薄煜琳，女，1990年生，硕士研究生，主要从事环境岩土工程方面的研究。
  • 基金资助:
    国家863计划课题（No. 2013AA06A206）；国家自然科学基金重点项目（No. 41330641）；国家自然科学基金项目（No. 51278100，No. 41472258）；江苏省自然科学基金杰出青年基金项目（No. BK2012022）。

Strength and leachability of lead contaminated clay stabilized by GGBS-MgO

BO Yu-lin1, 2, YU Bo-wei1, 2, DU Yan-jun1, 2, WEI Ming-li1, 2   

  1. 1. Institute of Geotechnical Engineering, Southeast University, Nanjing, Jiangsu 210096, China; 2. Jiangsu Key Laboratory of Urban Underground Engineering & Environmental Safety, Southeast University, Nanjing, Jiangsu 210096, China
  • Received:2014-12-31 Online:2015-10-10 Published:2018-06-13

PDF (Chinese)

1527

摘要： 以粒化高炉矿渣粉-氧化镁（GGBS-MgO）固化铅污染黏土为研究对象，通过半动态淋滤试验，对GGBS-MgO在酸雨作用下的强度特性及溶出特性进行研究。通过对GGBS-MgO固化铅污染黏土半动态淋滤后pH值、针刺深度、无侧限抗压强度及浸出液中[Pb]、[Ca]、[Mg]元素浓度的测试，分析淋滤液初始pH值、掺量以及含铅不含铅对GGBS-MgO固化土强度特性的影响，讨论了初始淋滤液pH值、固化剂掺量对GGBS-MgO固化铅污染土累积铅、钙、镁溶出质量以及铅有效扩散系数的影响规律。结果表明，半动态淋滤试验使试样无侧限抗压强度qu较标准养护39 d试样降低了2%～53%，且淋滤液初始pH=2对试样qu影响最大；在相同掺量、相同淋滤液初始pH值时，GGBS-MgO固化未污染土半动态淋滤后qu较水泥固化未污染土qu提高了12%～43%；且当固化剂掺量为18%时，固化铅污染土强度特性较水泥有明显优势，约为水泥固化铅污染土强度的1.3～1.8倍；且相同配比时，淋滤液初始pH=2表层的pH值约为pH=3、4、5、7的1/2；随着淋滤液初始pH值、半动态淋滤后qu及内部pH值的增加，针刺深度减小；针贯入阻力与qu存在幂指数关系。此外，累积铅、钙、镁溶出质量随着初始淋滤液pH值、固化剂掺量的增加而减少，在初始淋滤液pH=2时，Ai,Pb、Ai,Ca、Ai,Mg分别约为pH=3、4、5和7的29～222倍、1.7～4.4倍和12.0～80.3倍；固化剂掺量为12%时的累积溶出质量约是18%掺量时的1.1～2.0倍；铅有效扩散系数De随着初始淋滤液pH值的增加而降低，初始淋滤液pH=2时的De比pH=3～7的De高约3～5个数量级；且低于水泥固化铅污染土De，当初始淋滤液pH=7时，GGBS-MgO固化土De相比于水泥固化土低1～2个数量级。

关键词: 粒化高炉矿渣粉-氧化镁（GGBS-MgO）, 固化/稳定化, 半动态淋滤, 铅污染, 无侧限抗压强度, 有效扩散系数

Abstract: This paper investigates the effects of simulated acid rain on the strength and dissolution characteristics of lead contaminated clay, which is stabilized by GGBS-MgO (ground granulated blast furnace slag-magnesium oxide). Semi-dynamic leaching tests are conducted to measure the soil pH value, needle penetration depth, unconfined compressive strength and concentrations of lead, calcium and magnesium in leachate. Thus the effects of the initial pH of leachant, content of GGBS-MgO and lead contamination on the strength characteristics of GGBS-MgO stabilized clay are analyzed, and their effects on the cumulative mass of leached lead, calcium and magnesium and effective diffusion coefficient of lead are further determined. The results demonstrate that the unconfined compressive strength of clay using the semi-dynamic leaching tests is 2%-53% less, compared with the value under standard curing conditions for 39 days. Moreover, the highest impact on the strength of soil is found with an initial pH 2 of the leachant. Under the same content of GGBS-MgO and initial pH of leachant, the strength of the GGBS-MgO stabilized clay is approximately 12%-43% higher than that of the cement solidified clay. When the content of GGBS-MgO is 18%, the strength of clay stabilized by GGBS-MgO is almost 1.3-1.8 times of that of clay stabilized by cement. When the initial pH of leachant is 2, the pH at the specimen subsurface is approximately 50% of that when the pH values of leachant are from 3 to 7. The needle penetration depth decreases with increasing initial pH of leachant, qu and internal pH of clay. Furthermore, the relationship between needle penetration resistance and unconfined compressive strength fits unique power. In addition, the cumulative mass of leached lead, calcium and magnesium decreases with the increase of initial pH of leachant and the content of GGBS-MgO. When initial pH of leachant equals to 2, the cumulative mass of leached lead, calcium and magnesium is approximately 29-222, 1.7-4.4, 12.0-80.3 times of that when initial pH values of leachant are 3, 4, 5 and 7, respectively. Besides, when the content of GGBS-MgO is 12%, the cumulative mass is 1.1-2.0 times of that when the content is 18%. In addition, the effective diffusion coefficient of lead De decreases with the increase of the initial pH of leachant. When pH of leachant is 2, the De is 3-5 orders of magnitude higher than that of the pH values of leachant are 3, 4, 5 and 7. It is found that the De of lead contaminated clay stabilized by GGBS-MgO is lower than that of cement stabilized clay. Particularly, when the pH of leachant is 7, the De of the former one is 1-2 orders of magnitude lower than that of the later one.

Key words: ground granulated blast furnace slag-magnesium oxide (GGBS-MgO), solidification/stabilization, semi-dynamic leaching test, lead contamination, unconfined compressive strength, effective diffusion coefficient

中图分类号: 

  • TU 411，X53
[1] 高运昌, 高盟, 尹诗, . 聚氨酯固化海砂的静力特性试验研究[J]. 岩土力学, 2019, 40(S1): 231-236.
[2] 沈泰宇, 汪时机, 薛乐, 李贤, 何丙辉, . 微生物沉积碳酸钙固化砂质黏性紫色土试验研究[J]. 岩土力学, 2019, 40(8): 3115-3124.
[3] 查甫生, 刘晶晶, 许龙, 邓永锋, 杨成斌, 储诚富, . 水泥−粉煤灰固化/稳定重金属污染土的电阻率 特性试验研究[J]. 岩土力学, 2019, 40(12): 4573-4580.
[4] 吕擎峰, 周 刚, 王生新, 霍振升, 马 博, . 固化盐渍土核磁共振微观特征[J]. 岩土力学, 2019, 40(1): 245-249.
[5] 陈瑞锋，田高源，米栋云，董晓强,. 赤泥改性黄土的基本工程性质研究[J]. , 2018, 39(S1): 89-97.
[6] 张亭亭，王 平，李江山，万 勇，薛 强，王士权, . 养护龄期和铅含量对磷酸镁水泥固化/稳定化铅污染土的固稳性能影响规律及微观机制[J]. , 2018, 39(6): 2115-2123.
[7] 张文杰，楼晓红，高佳雯. 高塌落度防渗墙填料扩散系数快速测定的透析试验[J]. , 2018, 39(2): 523-528.
[8] 章定文，项 莲，曹智国, . CaO对钙矾石固化/稳定化重金属铅污染土的影响[J]. , 2018, 39(1): 29-35.
[9] 刘晋铭，欧忠文，肖寒冰，莫金川，杨康辉. 功能组分对固化土早期强度的影响研究[J]. , 2017, 38(3): 755-761.
[10] 邓友生，吴 鹏，赵明华，段邦政，. 基于最优含水率的聚丙烯纤维增强膨胀土强度研究[J]. , 2017, 38(2): 349-353.
[11] 孙潇昊，缪林昌，童天志，王呈呈, . 微生物沉积碳酸钙固化砂土试验研究[J]. , 2017, 38(11): 3225-3230.
[12] 张亭亭，李江山，王 平，黄 茜，薛 强. 磷酸镁水泥固化铅污染土的力学特性试验研究及微观机制[J]. , 2016, 37(S2): 279-286.
[13] 崔明娟，郑俊杰，赖汉江. 颗粒粒径对微生物固化砂土强度影响的试验研究[J]. , 2016, 37(S2): 397-402.
[14] 张亭亭，李江山，王 平，李振泽. 磷酸镁水泥固化铅污染土的应力-应变特性研究[J]. , 2016, 37(S1): 215-225.
[15] 杨康辉，欧忠文，肖寒冰，莫金川，刘晋铭. 水泥基渗透结晶型防水材料对硫铝酸盐水泥固化土性能影响及机制分析[J]. , 2016, 37(2): 477-486.
Viewed
Full text


Abstract

Cited
  Shared   
  Discussed   
[1] 刘小文，常立君，胡小荣. 非饱和红土基质吸力与含水率及密度关系试验研究[J]. , 2009, 30(11): 3302 -3306 .
[2] 黄建华，宋二祥. 大型锚碇基础围护工程冻结帷幕力学性态研究[J]. , 2009, 30(11): 3372 -3378 .
[3] 王观石，李长洪，陈保君，李世海. 应力波在非线性结构面介质中的传播规律[J]. , 2009, 30(12): 3747 -3752 .
[4] 王朝阳，许 强，倪万魁. 原状黄土CT试验中应力-应变关系的研究[J]. , 2010, 31(2): 387 -391 .
[5] 邓 琴，郭明伟，李春光，葛修润. 基于边界元法的边坡矢量和稳定分析[J]. , 2010, 31(6): 1971 -1976 .
[6] 万少石，年廷凯，蒋景彩，栾茂田. 边坡稳定强度折减有限元分析中的若干问题讨论[J]. , 2010, 31(7): 2283 -2288 .
[7] 闫 铁，李 玮，毕雪亮. 基于分形方法的多孔介质有效应力模型研究[J]. , 2010, 31(8): 2625 -2629 .
[8] 刘 嘉，王 栋. 正常固结黏土中平板锚基础的吸力和抗拉力[J]. , 2009, 30(3): 735 -740 .
[9] 赵尚毅，郑颖人，李安洪，邱文平，唐晓松，徐 俊. 多排埋入式抗滑桩在武隆县政府滑坡中的应用[J]. , 2009, 30(S1): 160 -164 .
[10] 刘振平，贺怀建，朱发华. 基于钻孔数据的三维可视化快速建模技术的研究[J]. , 2009, 30(S1): 260 -266 .
版权所有 © 《岩土力学》编辑部
地址：湖北武汉武昌小洪山中国科学院武汉岩土力学研究所(430071)　邮编：200042　电话：027-87198484, 87199252, 87199253, 87198752　E-mail: ytlx@whrsm.ac.cn
本系统由北京玛格泰克科技发展有限公司设计开发