基于最优含水率的聚丙烯纤维增强膨胀土强度研究

邓友生1, 2,吴 鹏2,赵明华3,段邦政2   

  1. 1.西安科技大学 建筑与土木工程学院,陕西 西安 710054;2.湖北工业大学 土木工程与建筑学院,湖北 武汉 430068; 3.湖南大学 岩土工程研究所,湖南 长沙 410082
  • 收稿日期:2015-05-07 出版日期:2017-02-11 发布日期:2018-06-05
  • 作者简介:邓友生,男,1969年生,博士,教授,主要主要从事基础工程的教学与研究
  • 基金资助:

    国家自然科学基金(No. 51378182)

Strength of expansive soil reinforced by polypropylene fiber under optimal water content

DENG You-sheng1, 2, WU Peng2, ZHAO Ming-hua3, DUAN Bang-zheng2   

  1. 1. School of Civil Engineering & Architecture, Xi'an University of Science and Technology, Xi'an, Shaanxi 710054, China; 2. School of Civil Engineering & Architecture, Hubei University of Technology, Wuhan, Hubei 430068, China; 3. Institute of Geotechnical Engineering, Hunan University, Changsha, Hunan 410082, China
  • Received:2015-05-07 Online:2017-02-11 Published:2018-06-05
  • Supported by:

    This work was supported by the National Natural Science Foundation of China (51378182).

摘要: 将不同长度的聚丙烯纤维按照0.0%、0.1%、0.2%、0.3%和0.4%的重量比分别掺入膨胀土中配制试样,通过大量的室内试验研究了聚丙烯纤维对膨胀土强度的影响规律。试验结果表明:随着纤维的加入,膨胀土的抗剪强度得到了明显的增强,且无侧限抗压强度也随着纤维含量的增加而急剧增加,但当纤维含量超过最优加筋量0.3%时,加筋膨胀土的无侧限抗压强度和抗剪强度反而呈现降低趋势。相同纤维含量的情况下,膨胀土的强度也会随着纤维长度的增加而明显增加,同时聚丙烯纤维还可以增加纤维复合膨胀土的峰值强度,延缓土样的破坏,其研究结果为膨胀土性质的改良提供一种可借鉴的方法。

关键词: 最优含水率, 膨胀土, 聚丙烯纤维, 抗剪强度, 无侧限抗压强度

Abstract: Many experiments are carried out to study strength of expansive soil reinforced by polypropylene fiber with different lengths and weight ratios of fiber to dry soil (0.0%, 0.1%, 0.2%, 0.3% and 0.4%), respectively. The results show that the shear strength of expansive soil is enhanced significantly by adding fiber, and the unconfined compressive strength increases dramatically with the increase of fiber contents. While the fiber content exceeds the optimal content 0.3%, the unconfined compressive strength and the shear strength all decrease. Under the condition of the same fiber content, the strength of expansive soil also increases significantly with the increase of fiber length. Polypropylene fiber can also improve the peak strength and fracture toughness of expansive soil, delay the destruction of expansive soil. The study results provide a useful method for improvement of expansive soil.

Key words: optimal water content, expansive soils, polypropylene fiber, shear strength, unconfined compressive strength

中图分类号: 

  • TU 443

[1] 桂跃, 吴承坤, 赵振兴, 刘声钧, 刘锐, 张秋敏. 微生物分解有机质作用对泥炭土工程性质的影响[J]. 岩土力学, 2020, 41(S1): 147-155.
[2] 刘杰, 杨玉婳, 姚海林, 卢正, 岳婵, . 基于不同改性方法的分散性黏土处治试验研究[J]. 岩土力学, 2020, 41(S1): 163-170.
[3] 邹先坚, 王益腾, 王川婴. 钻孔图像中岩石结构面三维形貌特征及 优势抗滑方向研究[J]. 岩土力学, 2020, 41(S1): 290-298.
[4] 骆赵刚, 汪时机, 杨振北, . 膨胀土湿干胀缩裂隙演化及其定量分析[J]. 岩土力学, 2020, 41(7): 2313-2323.
[5] 庄心善, 赵汉文, 王俊翔, 黄勇杰, 胡智. 循环荷载下重塑弱膨胀土滞回曲线 形态特征定量研究[J]. 岩土力学, 2020, 41(6): 1845-1854.
[6] 瑜璐, 杨庆, 杨钢, 张金利. 塑性极限分析鱼雷锚锚尖贯入阻力[J]. 岩土力学, 2020, 41(6): 1953-1962.
[7] 杨凯旋, 侯天顺. 击实试验类型对EPS颗粒轻量土击实特性的 影响规律[J]. 岩土力学, 2020, 41(6): 1971-1982.
[8] 李敏, 孟德骄, 姚昕妤. 基于温度效应下二灰固化石油污染滨海盐渍土 力学特性优化固化需求[J]. 岩土力学, 2020, 41(4): 1203-1210.
[9] 刘建民, 邱月, 郭婷婷, 宋文智, 谷川, . 饱和粉质黏土静剪强度与振动后 静剪强度对比研究[J]. 岩土力学, 2020, 41(3): 773-780.
[10] 涂园, 王奎华, 周建, 胡安峰, . 有效应力法和有效固结压力法在预压地基 强度计算中的应用[J]. 岩土力学, 2020, 41(2): 645-654.
[11] 李小刚, 朱长歧, 崔翔, 张珀瑜, 王睿, . 含碳酸盐混合砂的三轴剪切试验研究[J]. 岩土力学, 2020, 41(1): 123-131.
[12] 张晨阳, 谌民, 胡明鉴, 王新志, 唐健健, . 细颗粒组分含量对钙质砂抗剪强度的影响[J]. 岩土力学, 2019, 40(S1): 195-202.
[13] 王欢, 陈群, 王红鑫, 张文举, . 不同压实度和基质吸力的粉煤灰三轴试验研究[J]. 岩土力学, 2019, 40(S1): 224-230.
[14] 高运昌, 高盟, 尹诗, . 聚氨酯固化海砂的静力特性试验研究[J]. 岩土力学, 2019, 40(S1): 231-236.
[15] 谢辉辉, 许振浩, 刘清秉, 胡桂阳, . 干湿循环路径下弱膨胀土峰值及残余强度演化研究[J]. 岩土力学, 2019, 40(S1): 245-252.
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
No Suggested Reading articles found!