麦秸秆加筋材料抗拉性能的实验研究

›› 2010, Vol. 31 ›› Issue (1): 128-132.

麦秸秆加筋材料抗拉性能的实验研究

魏丽¹，柴寿喜¹，蔡宏洲¹，王晓燕²，李敏³，石茜³

1. 天津城市建设学院天津市软土特性与工程环境重点实验室，天津 300384；2. 中水北方勘测设计研究有限责任公司勘察院，天津 3002223； 3. 兰州大学西部灾害与环境力学教育部重点实验室，兰州 730000

收稿日期:2008-06-25 出版日期:2010-01-10 发布日期:2010-02-02
通讯作者: 柴寿喜，男，1962年生，博士，教授，从事滨海盐渍土的改性固化与加筋技术研究。 E-mail:chaishouxi@163.com
作者简介:魏丽，女，1979年生，硕士，讲师，从事滨海盐渍土的改性固化与加筋技术研究。
基金资助:
国家自然科学基金课题（No. 40772166）；天津市自然科学基金课题（No. 07JCYBJC12900）；天津市建设管理委员会科技项目（No. 2007-43）.

Research on tensility of wheat straw for reinforced material

WEI Li¹，CHAI Shou-xi¹，CAI Hong-zhou¹，WANG Xiao-yan²，LI Min³，SHI Qian³

1. Tianjin Key Laboratory of Soft Soil Characteristics and Engineering Environment, Tianjin Institute of Urban Construction, Tianjin 300384, China; 2. Institute of Investigation, China Water Resources, Beifang Investigation, Design and Research Co. Ltd., Tianjin 300222, China; 3. Key Laboratory of Mechanics on Disaster and Environment in Western China of Ministry of Education, Lanzhou University, Lanzhou 730000, China

Received:2008-06-25 Online:2010-01-10 Published:2010-02-02

摘要/Abstract

摘要：

加筋作用取决于筋材间的交织作用、筋土间的摩擦作用，以及加筋材料自身的抗拉性能。利用扫描电镜观察天然和经高分子材料SH胶浸泡后麦秸秆的结构，发现麦秸秆孔隙中渗入了胶液，并在麦秸秆的内外表面形成了胶膜。通过拉伸实验，测试了无茎节和1茎节麦秸秆在天然、浸海水、浸胶及浸胶后再浸海水4种工况下的极限拉力和极限延伸率。结果表明，无茎节麦秸秆的极限拉力和极限延伸率均高于1茎节麦秸秆的；浸胶与天然麦秸秆、浸胶干燥后再浸海水与直接浸海水的麦秸秆相比，前者的极限拉力和极限延伸率均高于后者，说明SH胶浸泡麦秸秆，使其抗拉性能得到增强。

关键词: 麦秸秆, 加筋材料, 极限拉力, 极限延伸率, 滨海盐渍土

Abstract:

Strength and stability of reinforced soil depends on intercrossing and tensility of reinforced materials, and friction between reinforced material and soil. By means of SEM photos, it is observed that SH agent is infiltrated through the pore of wheat straw, and adhered to its surface. For studying its tensility, maximum tensile and elongation of wheat straw with one stem node and without stem node, is tested in the condition of original, soaked in sea water, marinated in SH agent, and soaked in sea water after marinating in SH agent. It has been certified that the maximum tensile and elongation of wheat straw without stem node is more than that of wheat straw with one stem node. Respectively comparison on the marinated in SH agent and original, and soaked in sea water after marinating in SH agent and soaked in sea water, the maximum tensile and elongation of wheat straw marinated in SH agent is more than that of original wheat straw. SH agent benefits to increase the tensility of wheat straw.

Key words: wheat straw, reinforced material, maximum tensile, maximum elongation, inshore saline soil

中图分类号:

TU 450

魏丽，柴寿喜，蔡宏洲，王晓燕，李敏，石茜. 麦秸秆加筋材料抗拉性能的实验研究[J]. , 2010, 31(1): 128-132.

WEI Li，CHAI Shou-xi，CAI Hong-zhou，WANG Xiao-yan，LI Min3，SHI Qian. Research on tensility of wheat straw for reinforced material[J]. , 2010, 31(1): 128-132.

参考文献

相关文章 15

[1]	周芬，梁强，杜运兴. 单根无黏结预应力筋对加筋体力学性能的影响[J]. , 2018, 39(7): 2442-2450.
[2]	徐超，林潇，沈盼盼,. 桩承式加筋路堤张力膜效应模型试验研究[J]. , 2016, 37(7): 1825-1831.
[3]	费康，陈毅，王军军 . 桩承式路堤土拱效应发挥过程研究[J]. , 2013, 34(5): 1367-1374.
[4]	彭芳乐，华针，曹延波 , . 加筋材料动态松弛有限元模型的建立及应用[J]. , 2013, 34(11): 3277-3283.
[5]	柴寿喜，王沛，王晓燕. 麦秸秆布筋区域与截面形状下的加筋土抗剪强度[J]. , 2013, 34(1): 123-127.
[6]	李敏，柴寿喜，王晓燕，魏丽. 以强度增长率评价麦秸秆加筋盐渍土的加筋效果[J]. , 2011, 32(4): 1051-1056.
[7]	王沛，柴寿喜，王晓燕，魏丽，李敏. 麦秸秆加筋盐渍土重型击实效果的影响因素分析[J]. , 2011, 32(2): 448-452.
[8]	王沛，王晓燕，柴寿喜. 滨海盐渍土的固化方法及固化土的偏应力-应变[J]. , 2010, 31(12): 3939-3944.
[9]	杨继位，柴寿喜，王晓燕，魏丽，李敏. 以抗压强度确定麦秸秆加筋盐渍土的加筋条件[J]. , 2010, 31(10): 3260-3264.
[10]	柴寿喜，王晓燕，王沛，魏丽，仲晓梅，李芳. 含盐量对石灰固化滨海盐渍土微结构参数的影响[J]. , 2009, 30(2): 305-310.
[11]	柴寿喜，杨宝珠，王晓燕，王沛，仲晓梅，魏丽 . 含盐量对石灰固化滨海盐渍土力学强度影响试验研究[J]. , 2008, 29(7): 1769-1772.
[12]	柴寿喜，杨宝珠，王晓燕，魏丽，王沛，仲晓梅 . 渤海湾西岸滨海盐渍土的盐渍化特征分析[J]. , 2008, 29(5): 1217-1220.
[13]	柴寿喜，王晓燕，仲晓梅，郭英，王沛，李芳 . 含盐量对石灰固化滨海盐渍土稠度和击实性能的影响[J]. , 2008, 29(11): 3066-3070.
[14]	王志强，柴寿喜，仲晓梅，郭英，王晓燕，魏丽 . 多元逐步回归分析应用于固化土强度与微结构参数相关性评价[J]. , 2007, 28(8): 1650-1654.
[15]	柴寿喜，王沛，韩文峰，李芳，魏丽，王晓燕 . 高分子材料固化滨海盐渍土的强度与微结构研究[J]. , 2007, 28(6): 1067-1072.

Metrics

Viewed

Full text

Abstract

Cited

Shared

Discussed