全尾砂-废石混合回填膏体渗透特性试验研究

›› 2014, Vol. 35 ›› Issue (9): 2515-2521.

全尾砂-废石混合回填膏体渗透特性试验研究

孙伟^{1, 2}，吴爱祥^{1, 2}，王洪江^{1, 2}，王少勇^{1, 2}，李涛^{1, 2}，李公成^{1, 2}

1. 北京科技大学钢铁冶金新技术国家重点实验室，北京 100083；2. 北京科技大学土木与环境工程学院，北京 100083

收稿日期:2013-08-16 出版日期:2014-09-10 发布日期:2014-09-16
通讯作者: 吴爱祥，男，1963年生，博士，教授，博士生导师，主要从事散体力学及采矿工程方面的理论和实践工作。E-mail：wuaixiang@126.com E-mail:kmustsw@qq.com
作者简介:孙伟，男，1983年生，博士研究生，主要从事膏体充填及矿山废弃资源化方面的研究工作。
基金资助:
国家“十二五”科技支撑计划项目(No. 2012BAB08B02；No. 2013BAB02B05)；国家自然科学基金项目（No. 51374034；No. 51304011；No. 51374035）。

Experimental study of permeability characteristics of backfill paste mixed with unclassified tailings and waste rock

SUN Wei^{1, 2}, WU Ai-xiang^{1, 2}, WANG Hong-jiang^{1, 2}, WANG Shao-yong^{1, 2}, LI Tao^{1, 2}, LI Gong-cheng^{1, 2}

1. State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China; 2. School of Civil and Environmental Engineering, University of Science and Technology Beijing, Beijing 100083, China

Received:2013-08-16 Online:2014-09-10 Published:2014-09-16

摘要/Abstract

摘要： 塌陷区混合回填膏体是由全尾砂、废石人工制备得到的复合宽粒级散体，其渗透性能直接影响到塌陷区回填体稳定性及次生灾害发生的可能性。采用自制的渗透性试验装置，研究了废石含量、废石粒径对混合回填体渗透系数的影响，并对回填体固有特征参数（粒径小于0.075、0.02 mm颗粒含量、不均匀系数、平均粒径）与渗透系数之间关联性进行了研究。试验结果表明，回填膏体渗透系数随废石掺量及粒径增大而增加，细粒效应显著。回填体中粒径小于0.075、0.02 mm颗粒含量对其渗透性影响至关重要，与渗透系数呈负指数关系。渗透系数随值增大而增大。当 20时，渗透系数增加趋于稳定。给出了混合回填体渗透系数定量方程，其结果与试验结果较为一致。

关键词: 塌陷区, 混合回填体, 渗透系数, 细粒效应, 膏体

Abstract: The mixed backfill paste for subsidence area is a kind of artificial compound granular media which has wide size fraction and is made of unclassified tailings and waste rock; its permeability performance directly affects the stability of backfill body for subsidence area and other secondary disasters occurrence. Based on homemade experimental apparatus of permeability, the effects of the content of waste rock, waste rock particle size on permeability coefficient of mixed backfill body, and the relevance between backfill paste’s inherent characteristic parameters (the content of particle size below 0.075 mm and 0.02 mm, non-uniform coefficient , mean particle size) and permeability coefficient are studied. Test results show that, with waste rock content and particle size increasing, the permeability coefficient of backfill paste increases; the fine particle effect is remarkable. The content of particle size below 0.075 mm and 0.02 mm in backfill paste has a crucial effect on permeability and has a negative exponent relation with the permeability coefficient. Permeability coefficient increases along with the values. When the value is less than 20, permeability coefficient increases sharply; and when the value is greater than 20, the increase in permeability tends to be stable. Then the quantitative equation of mixed backfill paste permeability coefficient is obtained, which is consistent with the test results.

Key words: subsidence area, mixed backfilling, permeability coefficient, fine particle effect, paste

中图分类号:

TD 853

孙伟，吴爱祥，王洪江，王少勇，李涛，李公成 , . 全尾砂-废石混合回填膏体渗透特性试验研究[J]. , 2014, 35(9): 2515-2521.

SUN Wei , WU Ai-xiang , WANG Hong-jiang , WANG Shao-yong , LI Tao , LI Gong-cheng , . Experimental study of permeability characteristics of backfill paste mixed with unclassified tailings and waste rock[J]. , 2014, 35(9): 2515-2521.

参考文献

相关文章 15

[1]	李红坡, 陈征, 冯健雪, 蒙宇涵, 梅国雄, . 双层地基水平排水砂垫层位置优化研究[J]. 岩土力学, 2020, 41(2): 437-444.
[2]	彭家奕, 张家发, 沈振中, 叶加兵, . 颗粒形状对粗粒土孔隙特征和渗透性的影响[J]. 岩土力学, 2020, 41(2): 592-600.
[3]	王刚, 韦林邑, 魏星, 张建民, . 压实黏土三轴压缩变形过程中的渗透性变化规律[J]. 岩土力学, 2020, 41(1): 32-38.
[4]	刘丽, 吴羊, 陈立宏, 刘建坤, . 基于数值模拟的湿润锋前进法测量精度分析[J]. 岩土力学, 2019, 40(S1): 341-349.
[5]	徐浩青, 周爱兆, 姜朋明, 刘顺青, 宋苗苗, 陈亮, . 不同砂−膨润土垂直防渗墙填筑土料的掺量研究[J]. 岩土力学, 2019, 40(S1): 424-430.
[6]	张玉国, 万东阳, 郑言林, 韩帅, 杨晗玥, 段萌萌. 考虑径向渗透系数变化的真空预压竖井地基固结解析解[J]. 岩土力学, 2019, 40(9): 3533-3541.
[7]	胡明鉴, 崔翔, 王新志, 刘海峰, 杜韦, . 细颗粒对钙质砂渗透性的影响试验研究[J]. 岩土力学, 2019, 40(8): 2925-2930.
[8]	李贤, 汪时机, 何丙辉, 沈泰宇, . 土体适用MICP技术的渗透特性条件研究[J]. 岩土力学, 2019, 40(8): 2956-2964.
[9]	范日东, 刘松玉, 杜延军, . 基于改进滤失试验的重金属污染膨润土渗透特性试验研究[J]. 岩土力学, 2019, 40(8): 2989-2996.
[10]	余良贵, 周建, 温晓贵, 徐杰, 罗凌晖, . 利用HCA研究黏土渗透系数的标准探索[J]. 岩土力学, 2019, 40(6): 2293-2302.
[11]	陶高梁, 吴小康, 甘世朝, 肖衡林, 马强, 罗晨晨, . 不同初始孔隙比下非饱和黏土渗透性试验研究及模型预测[J]. 岩土力学, 2019, 40(5): 1761-1770.
[12]	张昭, 程靖轩, 刘奉银, 齐吉琳, 柴军瑞, 李会勇, . 基于土颗粒级配预测非饱和渗透系数函数的物理方法[J]. 岩土力学, 2019, 40(2): 549-560.
[13]	刘一飞, 郑东生, 杨兵, 祝兵, 孙明祥. 粒径及级配特性对土体渗透系数影响的细观模拟[J]. 岩土力学, 2019, 40(1): 403-412.
[14]	朱长歧, 崔翔, 胡明鉴, 王新志, 唐健健, . 钙质土电导率和渗透性的相关研究[J]. 岩土力学, 2018, 39(S2): 142-148.
[15]	马瑞男, 郭红仙, 程晓辉, 刘景儒, . 微生物拌和加固钙质砂渗透特性试验研究[J]. 岩土力学, 2018, 39(S2): 217-223.

Metrics

Viewed

Full text

Abstract

Cited

Shared

Discussed