重金属作用下改性水泥系隔离墙化学相容性研究

doi:10.16285/j.rsm.2022.0309

岩土力学 ›› 2023, Vol. 44 ›› Issue (2): 497-506.doi: 10.16285/j.rsm.2022.0309

重金属作用下改性水泥系隔离墙化学相容性研究

刘宜昭^{1, 2}，陆阳^{1, 3}，刘松玉^{1, 2}

1. 东南大学岩土工程研究所，江苏南京 210096；2. 东南大学江苏省城市地下工程与环境安全重点实验室，江苏南京 210096； 3. 深圳市大鹏新区住房和建设局，广东深圳 518000

收稿日期:2022-03-15 接受日期:2022-06-29 出版日期:2023-02-10 发布日期:2023-02-17
通讯作者: 刘松玉，男，1963年生，博士，教授，主要从事桩基工程、地基处理及环境岩土等方面的研究工作。E-mail: liusy@seu.edu.cn E-mail:lyz9558@foxmail.com
作者简介:刘宜昭，男，1995年生，博士研究生，主要从事环境岩土和地基处理等方面的科研工作。
基金资助:
江苏省交通运输科技项目（No. HTSQ(B)2021-249）

Study on chemical compatibility of amended cement-soil vertical cutoff wall permeated with heavy metal solutions

LIU Yi-zhao^{1, 2}, LU Yang^{1, 3}, LIU Song-yu^{1, 2}

1. Institute of Geotechnical Engineering, Southeast University, Nanjing, Jiangsu 210096, China; 2. Jiangsu Key Laboratory of Urban Underground Engineering and Environmental Safety, Southeast University, Nanjing, Jiangsu 210096, China; 3. Housing and Construction Bureau of Dapeng New District, Shenzhen, Guangdong 518000, China

Received:2022-03-15 Accepted:2022-06-29 Online:2023-02-10 Published:2023-02-17
Supported by:
This work was supported by the Transportation Science and Technology Project of Jiangsu Province (HTSQ(B)2021-249).

摘要/Abstract

摘要： 水泥系隔离墙被广泛应用于工业污染场地修复工程，但其防渗性能有待改善，且在高浓度、毒理性重金属污染作用下的化学相容性有待研究。通过室内试验研究了不同粒化高炉矿渣（GGBS）掺量、膨润土掺量和固化剂总掺量对水泥系隔离墙的强度和渗透特性的影响；综合考虑成墙效果和成本，选出固化剂掺量为20%（水泥、粒化高炉矿渣和膨润土掺量分别为8%、8%和4%）作为改性水泥系竖向隔离墙的最优配比。通过柔性壁渗透试验研究了重金属锌、铅污染作用下改性水泥系隔离墙试样的化学相容性。结果表明，重金属溶液作用下试样防渗性能的下降由重金属种类、重金属浓度以及试样孔隙液pH值三者共同决定。重金属种类对防渗性能的不利影响为：硝酸锌-硝酸铅>硝酸锌>硝酸铅。锌、铅溶液作用下试样的渗透系数为自来水作用下渗透系数的1.49～10.10倍，且重金属溶液的浓度越高渗透系数越大。在满足防渗要求前提下，该配比墙体材料能阻挡50 mmol/L的硝酸锌污染液、100 mmol/L的硝酸铅污染液和10 mmol/L硝酸锌-硝酸铅污染液。

关键词: 水泥土, 隔离墙, 重金属, 渗透系数, 化学相容性

Abstract: Cement-soil vertical cutoff wall is extensively applied to the remediation of industrial contaminated sites, but its impermeability needs to be improved and also the chemical compatibility under the effect of high concentration and toxic heavy metal contamination needs to be studied. Through laboratory tests, physical, strength and permeability properties of different cement-soil vertical cutoff wall samples based on different mixing ratios of GGBS (ground granulated blast furnace slag), bentonite, and curing agent were studied. Considering the quality of the vertical cutoff wall and economic cost, the curing agent dosage of 20% (the mixing ratios of PC, GGBS and bentonite are 8%, 8% and 4%, respectively) was validated as the optimal ratio for the amended cement-soil vertical cutoff wall. The chemical compatibility of cement-soil vertical cutoff wall materials under the effects of heavy metal zinc and lead pollution, in terms of hydraulic conductivity, is examined by a flexible-wall permeability test. The result shows that the decrease in the impermeability of the cement-soil vertical cutoff wall under the action of heavy metal solutions is jointly dominated by three factors, i.e., heavy metal species, the concentration of heavy metal, and the pH of pore solution. The adverse effect of the type of heavy metals on the impermeability of the samples is in this order: zinc nitrate-lead nitrate solution> zinc nitrate solution> lead nitrate solution. The hydraulic conductivities of the samples permeated with different heavy metal solutions are between 1.49 and 10.10 times that of sample permeated with tap water and increase with the increase of concentration of the heavy metal solution. Under the premise of meeting the requirement of hydraulic conductivity, the amended cement-soil vertical cutoff wall could barrier 50 mmol/L of zinc nitrate solution, 100 mmol/L of lead nitrate solution and 10 mmol/L of zinc nitrate-lead nitrate solution.

Key words: cement-soil, vertical cutoff wall, heavy metal, hydraulic conductivity, chemical compatibility

中图分类号:

X 53

刘宜昭, 陆阳, 刘松玉, . 重金属作用下改性水泥系隔离墙化学相容性研究[J]. 岩土力学, 2023, 44(2): 497-506.

LIU Yi-zhao, LU Yang, LIU Song-yu, . Study on chemical compatibility of amended cement-soil vertical cutoff wall permeated with heavy metal solutions[J]. Rock and Soil Mechanics, 2023, 44(2): 497-506.

参考文献

相关文章 15

[1]	文少杰, 郑文杰, 胡文乐, . 铅污染对黄土宏观持水性能和微观结构演化的影响研究[J]. 岩土力学, 2023, 44(2): 451-460.
[2]	潘振辉, 肖涛, 李萍, . 压实度与制样含水率对压实黄土微结构及水力特性的影响[J]. 岩土力学, 2022, 43(S1): 357-366.
[3]	贺桂成, 谢元辉, 李咏梅, 李春光, 唐孟媛, 张志军, 伍玲玲. 微生物胶结砂岩型铀矿砂的抗渗性能试验研究[J]. 岩土力学, 2022, 43(9): 2504-2514.
[4]	张小燕, 张益, 张晋勋, 魏凯园, 王宁, . 含橡胶纤维钙质砂的渗透和固结特性试验研究[J]. 岩土力学, 2022, 43(8): 2115-2122.
[5]	王海曼, 倪万魁. 不同干密度压实黄土的饱和/非饱和渗透系数预测模型[J]. 岩土力学, 2022, 43(3): 729-736.
[6]	周实际, 杜延军, 倪浩, 孙慧洋, 李江山, 杨玉玲, . 压实度对铁盐稳定化砷、锑污染土特性的影响及机制研究[J]. 岩土力学, 2022, 43(2): 432-442.
[7]	郑紫荆, 朱云海, 王巧, 谢海建, 陈赟, . 有机污染物在含土工膜复合隔离墙和含水层系统的运移半解析模型[J]. 岩土力学, 2022, 43(2): 453-465.
[8]	SUKSAN Aniroot, HORPIBULSUK Suksun, . 水泥稳定再生沥青路面/红土混合物用于软土改良的效果评估[J]. 岩土力学, 2022, 43(12): 3305-3315.
[9]	蒋小虎, 黄跃廷, 胡海军, 陈铄, 陈锐, 王崇华, 汪慧, 康顺祥, . 基于原位双环、试坑浸水试验和数值模拟反演的Q3黄土饱和渗透系数对比研究[J]. 岩土力学, 2022, 43(11): 2941-2951.
[10]	刘阿强, 李旭, 刘艳, 张志远. 全吸力范围内渗透系数快速测定方法研究[J]. 岩土力学, 2022, 43(11): 3209-3219.
[11]	雷华阳, 许英刚, 蒋明镜, 刘旭, 缪姜燕, . 动渗耦合作用下软黏土渗透系数演化机制分析[J]. 岩土力学, 2022, 43(10): 2665-2674.
[12]	刘金都, 冯晨, 李江山, 汪凯凯, . 砷、镉复合重金属污染土土−水特性及微观机制研究[J]. 岩土力学, 2022, 43(10): 2841-2851.
[13]	詹良通, 丁兆华, 谢世平, 李育超, 何顺辉, . 竖向阻隔墙中土工复合膨润土防水毯搭接区渗透系数测试与分析[J]. 岩土力学, 2021, 42(9): 2387-2394.
[14]	刘丽, 吴羊, 李旭, 赵煜鑫, . 压实度对宽级配土水力特性的影响研究[J]. 岩土力学, 2021, 42(9): 2545-2555.
[15]	万志辉, 戴国亮, 龚维明, 高鲁超, . 海水环境下钙质砂水泥土加固体的微观侵蚀机制试验研究[J]. 岩土力学, 2021, 42(7): 1871-1882.

Metrics

Viewed

Full text

Abstract

Cited

Shared

Discussed

重金属作用下改性水泥系隔离墙化学相容性研究

Study on chemical compatibility of amended cement-soil vertical cutoff wall permeated with heavy metal solutions

PDF (Chinese)

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

Metrics

本文评价

推荐阅读 10